Benefits | ||||||||||||||||
|
Properties | |
Curing | |
Work life at 23°C |
2 hours (4g in syringe) |
Curing schedule (time to full cure) |
24 hours at 25°C 20 minutes at 75°C 5 minutes at 100°C |
Properties before curing | |
Mixed viscosity | 0.5 ÷ 1.5 Pa·s |
Surface tension | 42 - 44 mN/m |
Optimum properties (cured for 5' at 100°C) | |
Glass transition temperature |
105°C |
Thermal expansion | 55 x 10-6 cm/cm/°C |
Density | 1.1 |
Hardness | 85D |
Lap shear (Al/Al) | 11 MPa |
Operating temperature |
-60°C to +200°C |