Benefits | ||||||||||||||||
|
Properties | |
Curing | |
Work life at 23°C |
12 hours |
Pre-cure gelling | 2 hours at 80°C |
Curing schedule (time to full cure) |
30 minutes at 135°C 15 minutes at 150°C |
Properties before curing | |
Mixed viscosity | 15 Pa·s |
Optimum properties (cured for 15' at 150°C) | |
Glass transition temperature |
> 150°C |
Thermal expansion |
55 x 10-6 cm/cm/°C |
Density | 1.25 |
Hardness | 92D |
Modulus | 2 GPa |
Shrinkage on cure | < 3.5% |
Operating temperature |
-60°C to +250°C |